$1700≥1Others
| Tipo di pagamento: | T/T |
| Quantità di ordine minimo: | 1 ton |
| Porta: | Shanghai Port |
Ombra:
Modello: TM-2001
marchio: Tc
CAS No.: 25608-12-2
Other Names: unsaturated polyester resin for boat
MF: C3H5NO)n
EINECS No.: 208-750-2
Type: Synthetic Resin And Plastics
Brand Name: Fullmark
Model Number: TC-196, TC-196
Appearance: Light yellow transparent liquid
Pacchetto: metal barrel
Utilizzo: unsaturated polyester resin for boat
Net Weight: 220kg
Certificati : Msds
Storage Period: 90 days .but it's 30 days if add thixotropice accelerator
Storage Condition: Below 25℃ in dark
Elenco prodotti correlati: unsaturated polyester resin for boat
Place Of Origin: Jiangsu, China
Purity: 61-67%
marchio: Fullmark
| Unità vendibili | : | ton |
| Tipo pacchetto | : | barile di metallo |
| Esempio immagine | : |
|
The file is encrypted. Please fill in the following information to continue accessing it
Resina in poliestere insaturi TC-K196
Descrizione del prodotto
Resina in poliestere insaturi per uso generale TC196, buona impregnazione in fibra di vetro, buona resistenza ai raggi UV e resistenza meccanica.
Proprietà in resina poliestere liquida insaturata
|
Item |
Unit |
Measured data |
Testing method |
|
Appearance |
- |
Light yellow transparent liquid |
GB-T 8237.4.1.1 |
|
viscosity |
25℃,Pa·s |
0.25-0.45 |
GB/T 7193.1 |
|
Gel time |
25℃,min |
9-17 |
GB/T 7193.6 |
|
Acid value |
mgKOH/g |
28-36 |
GB/T 2895 |
|
Solid content |
% |
61-67 |
GB/T 7193.3 |
Tempo di gel: 50% perossido di cicloesanone: 4%; Acceleratore E1: 4%;
Proprietà del corpo del casting in resina
|
Item |
Measured data |
Unit |
Testing method |
|
Barcol hardness |
46 |
— |
GB 3854-83 |
|
Distortion temperature |
66 |
℃ |
GB 1634-04 |
|
Elongation at break |
1.8 |
% |
GB 2568-95 |
|
Notes:1)casting body sample preparation method according to GB 8237-87,curing system:hardener 55%MEKPO:2%,promoter E1; 2)post cure system:60℃×2h+80℃×2h. |
|||
Proprietà fisica FRP
|
Item |
Unit |
Measured data |
Testing method |
|
Bending strength |
MPa |
325 |
GB/T2570-95 |
|
Bending modulus |
MPa |
1.40×104 |
GB/T2570-95 |
|
Notes:1)casting body sample preparation method according to GB 8237-87,curing system:hardener 55%MEKPO:2%,promoter E1; 2)post cure system:60℃×3h+110℃×3h. |
|||
Pacchetto di resina e condizioni di archiviazione
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Contact Now